膜科学与技术

半互穿网络法亲水改性超滤膜

作者：陈亚，钱欣，周勇，高从堦

单位： 1.浙江工业大学化材学院，浙江杭州，310014；2.杭州水处理技术研究开发中心，310012

关键词：聚砜；水通量；PVP；络合剂

出版年,卷(期):页码： 2010,30(6):0-0

摘要：

摘要：以聚砜（PSF）为膜材料，水为凝胶剂，采用浸没沉淀相转化法制备PSF超滤膜，在制膜过程中添加了亲水性聚合物聚乙烯基吡咯烷酮（PVP）和络合剂FeCl2来改性PSF膜的亲水性，并对其性能进行表征。用红外来表征其络合性能，用接触角测量仪测定其亲水性能。探讨了PSF含量，络合剂FeCl2用量，PVP用量，PVP分子量对超滤膜性能的影响。结果表明，增加PSF含量，膜的通量变小；增加络合剂FeCl2的含量，膜的通量由大变小，是没有加络合剂的1.3倍；增加PVP的含量，膜的亲水性得到了显著的提高。在4%的时候为最大，此时的通量比没加PVP的膜大11倍。而对于不同牌号的PVP，K60的通量最大，K90的最小。对牛血清蛋白(BSA)的截留率都达到了95%以上。

Abstract: Polysulfone blend membranes are fabricated by phase inversion process from casting solution of PSF, pure water as non-solvent. Add Polyvinyl pyrrolidone and FeCl2 into casting solution is order to change hydrophilic of polysulfone membrane in membrane process. Complextion characterization was performanced by IR and SEM, hydrophilic characterization was performanced by contact angle machine. The morphology of the membrane was controlled by changing the concentration of PSF, kinds of pvp, concentration of FeCl2 and so on. It was found that the membrace morphologies were changes by pvp and FeCl2 obviously. The parameters for membrane fabrication with good performances were summarized. The rate of rejection to bovine serum album(BSA) in solution(1g/L) is above 95%.

陈亚（1986—），男，江苏连云港市人，硕士研究生,主要从事超滤膜研究。

参考文献：

参考文献
[1] Qin J J , Wong F S , Liu Y,Liu Y T. A high flux ultrafiltration membrane spun f rom PSF/ PVP ( k90) / DMF/ 1 , 2-propanediol [ J ] . J. Membr. sci .2003. 211: 139-1471
[2] 柯林楠吴光夏续曙光,聚砜/ 聚醚类高聚物共混相容性及超滤膜的研究[J],膜科学也技术,2005,25(3),5-9.
[3] Yoo J E , Kim J H , Kim Y, et al . Novel ultrafiltr- ationmembranes prepared from the new miscible blends of polysulfone with poly ( 1- vinylpyrro- lidone-co-styrene)copolymers[J ] . J Membr Sci , 2003 , 216 : 95 - 106.
[4] 杨亚楠李良飞杨海东等,PSF/PEG共混超滤膜的性能研究[J],长春工业大学学报，2006，27(4)，298-301
[5] srimanta pal et al, Characterization of CO2 plasma treated polymeric membranes and quantification of flux enhancement[J] ,J Membr Sci,2008,323：1-10
[6] Ulbricht Belfort G. J. Suface modification of ultra- filtration membrances by low temperature plasma [J],Membr. Sci, 1996, 111(2): 193~215
[7] Kim K. S., Lee K. H., Cho K. et al., Suface modif- ication of polysulfone ultrafiltration memb- rance by oxygen plasma treatment [J],J. Membr. Sci. 2002, 199(4): 135~145
[8] 杨牛珍等聚丙烯腈超滤膜低温氧等离子体表面改性西北纺织工学院学报 [J], 2000, 14(3): 314~317
[9] Mathias Ulbricht .et al. Photo-induced graft poly -merrrization surface modifications for the prepa- ration of hydrophilic and low–protein-adsorbing ultrafiltration memebranes[J] ,J. Membr. Sci. [J], 1996, 115(12): 31~47
[10] 陆晓峰刘光全等,紫外辐射改性聚砜超滤膜[J],膜科学与技术,1998,18(5):49-54
[11] Komaki Y., Radicals in heavy ion-irradiated polyvinylidene fluoride [J],Radiat Means 1996, 26(1): 123~129
[12] 何昌生, 孙雪雁.小孔径磺化聚砜超滤膜的研制,水处理技术 [J], 1998, 24(5): 265~269
[13] Han S, Membranes & Membrane Processes [M], New York: Plenum Press, NY, 1986, P143~150
[14] 董春华等,接枝丙烯酸亲水化改性聚砜超滤膜及其在多肽分离中的应用[J].化工学报2007, 58(6):1501~1506
[15] Morel G., Quazzani N., Graciaa A. et al., Sufact -ant modified ultrafiltration for nitrate ion removal [J],J. Membr. Sci. 1997, 134(7): 47~57
[16] 韩式荆, 刘忠洲, 刘建维, 表面活性剂对膜分离行为的影响,水处理技术 [J], 1989, 5(2): 87 ~92
[17] 王洪军, 刘家祺, 李俊台, PVA/PS中空纤维复合膜脱除丙烯中微量水分的研究[J],石油化工 2003, 31(11): 957~961
[18] 俞三传, 高从 .多元合金超滤膜的研制[J ] . 膜科学与技术, 2001 , 21 (2) :10 - 13.
[19] 吴开芬, 李书申, 韩式荆. 聚醚砜- 磺化聚砜共混膜的研究[J ] . 环境化学, 1993 , 12 (6) : 458 - 462
[20] 施柳青, 谢德峰, 刘光全,等. 磺化聚醚砜(SPES) / 聚醚砜(PES)合金超滤膜的研究[J ] . 净水处理,2000 ,19 (4) :16 - 19
[21] 宋艳秋, 原续波, 盛京, 疏水聚砜膜的共混改性研究[J].化学工业与工程, 2002, 19(1): 32~36
[23] 中本一雄.无机和配位化合物的红外和拉曼光谱[M].化学工业出版社.1991.342-346

服务与反馈：

【文章下载】【加入收藏】

《膜科学与技术》编辑部地址：北京市朝阳区北三环东路19号蓝星大厦邮政编码：100029 电话：010-64426130/64433466 传真：010-80485372邮箱：mkxyjs@163.com