膜科学与技术

高性能内压式中空纤维纳滤膜的制备及其性能

作者：刘少校，吕兴华，王恩琳，刘立扬，李树轩，苏保卫

单位：中国海洋大学化学化工学院/海洋化学理论与工程技术教育部重点实验室，山东青岛266100

关键词：纳滤膜；中空纤维；重金属离子；内压式

出版年,卷(期):页码： 2022,42(4):9-21

摘要：

纳滤（NF）膜在海水软化和废水回收利用等方面已经被广泛应用。内压式中空纤维（HF）NF膜因其填充密度大、皮层不易被破坏等特点具有广阔的发展前景。以自制的聚砜（PSf）HF超滤（UF）膜为基膜，采用界面聚合（IP）法，分别以哌嗪（PIP）和均苯三甲酰氯（TMC）为水相和油相单体，以十二烷基硫酸钠（SDS）和三乙胺（TEA）为水相添加剂，在基膜内表面完成IP反应，制备出内压式HFNF膜。考察了水相流速、氮气吹扫时间、PIP浓度以及TEA浓度对内压式HFNF膜分离性能的影响。结果表明，最优条件下制备的内压式HFNF膜在0.4 MPa的测试条件下，对于2000 mg/L的硫酸钠（Na2SO4）溶液中的Na2SO4截留率可达97.3%，水渗透率达93 L/（m2 h MPa）；对于2000 mg/L的硫酸锌（ZnSO4）、硫酸锰（MnSO4）溶液中的ZnSO4、MnSO4的截留率均达到93%以上。所制备的内压式HFNF膜有良好的耐污染性能和耐氯性能。

Nanofiltration (NF) membrane has been widely used in seawater softening and wastewater recycling. Internally pressurized hollow fiber (HF) NF membrane has broad development prospects as it possesses high filling density and difficult to damage the polyamide layer. In this paper, Polysulfone (PSf) HF ultrafiltration membrane was used as the substrate membrane, the internally pressurized HFNF membrane was prepared by interfacial polymerization (IP) on the inner surface of the substrate membrane with piperazine (PIP) and Trimesoyl chloride (TMC) as aqueous and organic monomers and Sodium dodecyl sulfate (SDS) and triethylamine (TEA) as aqueous additives. The effects of water phase flow rate, N2 purging time, PIP concentration and TEA concentration on the separation performance of internally pressurized HFNF membrane were studied. The performance test results showed that the internally pressurized HFNF membrane prepared under the optimal conditions had higher water permeability of 93 L/ (m2 h MPa) and the Na2SO4 rejection of 97.2% for 2000 mg/L Na2SO4 solution at 0.4 MPa. For 2000 mg/L heavy metal salt solution, the rejection of ZnSO4 and MnSO4 in ZnSO4 and MnSO4 solution could reach 93%. Moreover, the prepared internally pressurized HFNF membrane showed good anti-fouling performance and chlorine resistance performance.

刘少校（1997-），男，山东青岛人，硕士研究生，研究方向：中空纤维纳滤膜分离技术E-mail:lsx158799@foxmail.com

参考文献：

[1] ZHOU D, ZHU L, FU Y, et al. Development of lower cost seawater desalination processes using nanofiltration technologies — A review [J]. Desalination, 2015, 376: 109-116.
[2] 张金苗. 共价层层自组装纳滤膜的制备及性能研究 [J]. 膜科学与技术, 2020, 40(1): 139-147.
[3] LUO J, WAN Y. Effects of pH and salt on nanofiltration—a critical review [J]. Journal of Membrane Science, 2013, 438: 18-28.
[4] BARGEMAN G. Recent developments in the preparation of improved nanofiltration membranes for extreme pH conditions [J]. Separation and Purification Technology, 2021, 279: 119725-119761.
[5] JI C, ZHAI Z, JIANG C, et al. Recent advances in high-performance TFC membranes: A review of the functional interlayers [J]. Desalination, 2021, 500: 114869-114891.
[6] WEI X, XU X, CHEN Y, et al. Preparation and properties of hollow fibre nanofiltration membrane with continuous coffee-ring structure [J]. Frontiers of Chemical Science and Engineering, 2021, 15: 351-362.
[7] SHI W, LI T, LI H, et al. An attempt to enhance water flux of hollow fiber polyamide composite nanofiltration membrane by the incorporation of hydrophilic and compatible PPTA/PSF microparticles [J]. Separation and Purification Technology, 2022, 280: 119821-119839.
[8] LI H, SHI W, ZHANG H, et al. Preparation of internally pressurized polyamide thin-film composite hollow fiber nanofiltration membrane with high ions selectivity by a facile coating method [J]. Progress in Organic Coatings, 2020, 139: 105456-115469.
[9] TIAN L, JIANG Y, LI S, et al. Graphene oxide interlayered thin-film nanocomposite hollow fiber nanofiltration membranes with enhanced aqueous electrolyte separation performance [J]. Separation and Purification Technology, 2020, 248: 117153-117167.
[10] JIANG Y, LI S, SU J, et al. Two dimensional COFs as ultra-thin interlayer to build TFN hollow fiber nanofiltration membrane for desalination and heavy metal wastewater treatment [J]. Journal of Membrane Science, 2021, 635: 119523-119537.
[11] SU J, LV X, LI S, et al. High separation performance thin film composite and thin film nanocomposite hollow fiber membranes via interfacial polymerization for organic solvent nanofiltration [J]. Separation and Purification Technology, 2021: 119567-119580.
[12] GHERASIM C V, LUELF T, ROTH H, et al. Dual-Charged Hollow Fiber Membranes for Low-Pressure Nanofiltration Based on Polyelectrolyte Complexes: One-Step Fabrication with Tailored Functionalities [J]. ACS applied materials & interfaces, 2016, 8(29): 19145-19157.
[13] LI H, WANG W, ZHANG Y. Preparation and characterization of high-selectivity hollow fiber composite nanofiltration membrane by two-way coating technique [J]. Journal of Applied Polymer Science, 2014, 131(23): 41187-41198.
[14] BACK J O, SPRUCK M, KOCH M, et al. Poly(piperazine-amide)/PES Composite Multi-Channel Capillary Membranes for Low-Pressure Nanofiltration [J]. Polymers, 2017, 9(12): 1-15.
[15] TSAI H-A, CHEN Y-L, HUANG S-H, et al. Preparation of polyamide/polyacrylonitrile composite hollow fiber membrane by synchronous procedure of spinning and interfacial polymerization [J]. Journal of Membrane Science, 2018, 551: 261-272.
[16] LI X, WANG Z, HAN X, et al. Regulating the interfacial polymerization process toward high-performance polyamide thin-film composite reverse osmosis and nanofiltration membranes: A review [J]. Journal of Membrane Science, 2021, 640: 119765-119789.
[17] LIU Y-L, ZHAO Y-Y, WANG X-M, et al. Effect of varying piperazine concentration and post-modification on prepared nanofiltration membranes in selectively rejecting organic micropollutants and salts [J]. Journal of Membrane Science, 2019, 582: 274-283.
[18] SAHA N K, JOSHI S V. Performance evaluation of thin film composite polyamide nanofiltration membrane with variation in monomer type [J]. Journal of Membrane Science, 2009, 342(1-2): 60-69.
[19] NADLER R, SREBNIK S. Molecular simulation of polyamide synthesis by interfacial polymerization [J]. Journal of Membrane Science, 2008, 315(1-2): 100-105.
[20] YANG F, ZHANG S, YANG D, et al. Preparation and characterization of polypiperazine amide/PPESK hollow fiber composite nanofiltration membrane [J]. Journal of Membrane Science, 2007, 301(1-2): 85-92.
[21] ANG M B M Y, TANG C-L, DE GUZMAN M R, et al. Improved performance of thin-film nanofiltration membranes fabricated with the intervention of surfactants having different structures for water treatment [J]. Desalination, 2020, 481: 114352-114362.
[22] LIANG Y, ZHU Y, LIU C, et al. Polyamide nanofiltration membrane with highly uniform sub-nanometre pores for sub-1 A precision separation [J]. Nat Commun, 2020, 11(1): 2015-2024.
[23] PARK S-H, KWON S J, SHIN M G, et al. Polyethylene-supported high performance reverse osmosis membranes with enhanced mechanical and chemical durability [J]. Desalination, 2018, 436: 28-38.
[24] JEGAL J, MIN S G, LEE K-H. Factors affecting the interfacial polymerization of polyamide active layers for the formation of polyamide composite membranes [J]. Journal of Applied Polymer Science, 2002, 86(11): 2781-2787.
[25] KAMADA T, OHARA T, SHINTANI T, et al. Optimizing the preparation of multi-layered polyamide membrane via the addition of a co-solvent [J]. Journal of Membrane Science, 2014, 453: 489-497.
[26] KONG C, KANEZASHI M, YAMOMOTO T, et al. Controlled synthesis of high performance polyamide membrane with thin dense layer for water desalination [J]. Journal of Membrane Science, 2010, 362(1-2): 76-80.
[27] MOJALLALI ROSTAMI S M, AKBARI A. Development of permeability properties of polyamide thin film composite nanofiltration membrane by using the dimethyl sulfoxide additive [J]. Journal of Water Reuse and Desalination, 2014, 4(3): 174-181.
[28] ZHU W-P, GAO J, SUN S-P, et al. Poly(amidoamine) dendrimer (PAMAM) grafted on thin film composite (TFC) nanofiltration (NF) hollow fiber membranes for heavy metal removal [J]. Journal of Membrane Science, 2015, 487: 117-126.
[29] HURWITZ G, GUILLEN G R, HOEK E. Probing polyamide membrane surface charge, zeta potential, wettability, and hydrophilicity with contact angle measurements [J]. Journal of membrane science, 2010, 349(1-2): 349-357.
[30] YAROSHCHUK A, RIBITSCH V. Role of Channel Wall Conductance in the Determination of ζ-Potential from Electrokinetic Measurements [J]. Langmuir, 2002, 18：2036-2038.
[31] AFONSO M D. Streaming potential measurements to assess the variation of nanofiltration membranes surface charge with the concentration of salt solutions [J]. Separation and Purification Technology, 2001, 22-23: 529–541.
[32] CHEN M, XIAO C, WANG C, et al. Preparation and characterization of a novel thermally stable thin film composite nanofiltration membrane with poly (m-phenyleneisophthalamide) (PMIA) substrate [J]. Journal of Membrane Science, 2018, 550: 36-44.
[33] LI L, ZHANG S, ZHANG X. Preparation and characterization of poly(piperazineamide) composite nanofiltration membrane by interfacial polymerization of 3,3′,5,5′-biphenyl tetraacyl chloride and piperazine [J]. Journal of Membrane Science, 2009, 335(1-2): 133-139.
[34] KHORSHIDI B, THUNDAT T, PERNITSKY D, et al. A parametric study on the synergistic impacts of chemical additives on permeation properties of thin film composite polyamide membrane [J]. Journal of Membrane Science, 2017, 535: 248-257.
[35] HERMANS S, BERNSTEIN R, VOLODIN A, et al. Study of synthesis parameters and active layer morphology of interfacially polymerized polyamide–polysulfone membranes [J]. Reactive and Functional Polymers, 2015, 86: 199-208.
[36] RAHIMPOUR A, JAHANSHAHI M, PEYRAVI M, et al. Interlaboratory studies of highly permeable thin-film composite polyamide nanofiltration membrane [J]. Polymers for Advanced Technologies, 2012, 23(5): 884-893.
[37] HERMANS S, MARIëN H, DOM E, et al. Simplified synthesis route for interfacially polymerized polyamide membranes [J]. Journal of Membrane Science, 2014, 451: 148-156.
[38] LIU M, YU S, TAO J, et al. Preparation, structure characteristics and separation properties of thin-film composite polyamide-urethane seawater reverse osmosis membrane [J]. Journal of Membrane Science, 2008, 325(2): 947-956.
[39] TANG A, FANG C, FENG W, et al. Engineering novel thin-film composite membranes with crater-like surface morphology using rigidly-contorted monomer for high flux nanofiltration [J]. Desalination, 2021, 509: 115067-115079.
[40] MASAHIKO HIROSE * H I, YOSHIYASU KAMIYAMA. Effect of skin layer surface structures on the flux behaviour of RO membranes [J]. Journal of Membrane Science, 1996, 121: 209-215.
[41] WANG Z, WANG Z, LIN S, et al. Nanoparticle-templated nanofiltration membranes for ultrahigh performance desalination [J]. Nat Commun, 2018, 9(1): 2004-2013.
[42] REN X, ZHAO C, DU S, et al. Fabrication of asymmetric poly (m-phenylene isophthalamide) nanofiltration membrane for chromium(VI) removal [J]. Journal of Environmental Sciences, 2010, 22(9): 1335-1341.
[43] ZHANG H-Z, XU Z-L, SHEN Q. High-performance nanofiltration membrane intercalated by FeOOH nanorods for water nanofiltration [J]. Desalination, 2021, 498: 114802-114813.
[44] ZHOU B-W, ZHANG H-Z, XU Z-L, et al. Interfacial polymerization on PES hollow fiber membranes using mixed diamines for nanofiltration removal of salts containing oxyanions and ferric ions [J]. Desalination, 2016, 394: 176-184.
[45] ZHANG J, LI S, REN D, et al. Fabrication of ultra-smooth thin-film composite nanofiltration membrane with enhanced selectivity and permeability on interlayer of hybrid polyvinyl alcohol and graphene oxide [J]. Separation and Purification Technology, 2021, 268: 118649-118663.
[46] WANG X-L, WEI J-F, DAI Z, et al. Preparation and characterization of negatively charged hollow fiber nanofiltration membrane by plasma-induced graft polymerization [J]. Desalination, 2012, 286: 138-144.
[47] YU W-H, GAN Z-Q, WANG J-R, et al. A novel negatively charged nanofiltration membrane with improved and stable rejection of Cr (VI) and phosphate under different pH conditions [J]. Journal of Membrane Science, 2021, 639:119756-119766.
[48] ZHANG S, FU F, CHUNG T-S. Substrate modifications and alcohol treatment on thin film composite membranes for osmotic power [J]. Chemical Engineering Science, 2013, 87: 40-50.
[49] WEI X, WANG Z, XU J, et al. Surface Modification of Commercial Aromatic Polyamide Reverse Osmosis Membranes by Crosslinking Treatments [J]. Chinese Journal of Chemical Engineering, 2013, 21(5): 473-484.
[50] YANG T, WANG K-Y, CHUNG T-S. Fabrication of thin-film composite hollow fiber membranes in modules for concentrating pharmaceuticals and separating sulphate from high salinity brine in the chlor-alkali process [J]. Journal of Membrane Science, 2021, 640: 119822-119832.
[51] ZHANG H-Z, XU Z-L, TANG Y-J, et al. Highly chlorine-tolerant performance of three-channel capillary nanofiltration membrane with inner skin layer [J]. Journal of Membrane Science, 2017, 527: 111-120.
[52] SHAO W, LIU C, MA H, et al. Fabrication of pH-sensitive thin-film nanocomposite nanofiltration membranes with enhanced performance by incorporating amine-functionalized graphene oxide [J]. Applied Surface Science, 2019, 487: 1209-1221.
[53] SOYEKWO F, LIU C, WEN H, et al. Construction of an electroneutral zinc incorporated polymer network nanocomposite membrane with enhanced selectivity for salt/dye separation [J]. Chemical Engineering Journal, 2020, 380: 122560-122574.
[54] KONG X, ZHOU M-Y, LIN C-E, et al. Polyamide/PVC based composite hollow fiber nanofiltration membranes: Effect of substrate on properties and performance [J]. Journal of Membrane Science, 2016, 505: 231-240.

服务与反馈：

【文章下载】【加入收藏】

《膜科学与技术》编辑部地址：北京市朝阳区北三环东路19号蓝星大厦邮政编码：100029 电话：010-64426130/64433466 传真：010-80485372邮箱：mkxyjs@163.com