PVC膜表面均匀孔结构形成原因初探

作者：王昌萌，史乐，阎安，武春瑞，吕晓龙

单位：天津工业大学，省部共建分离膜与膜过程国家重点实验室，材料科学与工程学院，天津 300387

关键词： PVC膜；非溶剂致相分离法；均匀孔结构；微孔膜

出版年,卷(期):页码： 2022,42(4):59-64

摘要：

通过在铸膜液中引入乙二胺(EDA)，促进聚氯乙烯（PVC）分子链发生消去反应，形成碳碳双键；进而通过相分离成膜，在PVC膜表面获得较均匀开孔结构。重点研究了EDA添加量、反应温度与时间等对膜表面孔结构及均一性的影响规律，利用原子力-红外联用、扫描电镜、X-射线光电子能谱等分析了PVC膜表面物理化学结构及分布规律，初步探索了PVC膜表面较均匀孔结构的形成原理。研究发现， EDA添加量的增加、反应温度升高、反应时间的增长均可以促进PVC膜表面孔径增大，均一性提升。

In this paper, ethylenediamine (EDA) was introduced into the casting solution to promote the elimination reaction of polyvinyl chloride (PVC) molecular chains to form carbon carbon double bond, and then the film was formed by phase separation to obtain a more uniform pore structure on the surface of PVC membranes. The effects of EDA addition, reaction temperature and time on the pore structure and uniformity of PVC membrane surface were studied. The physicochemical structure and distribution of PVC membrane surface were analyzed by atomic force infrared spectroscopy, scanning electron microscopy and X-ray photoelectron spectroscopy. It is found that with the increase of EDA addition, the increase of reaction temperature and reaction time can promote the increase of PVC membrane surface pore size and uniformity.

王昌萌（1994-），男，山东郓城人，硕士生，主要从事膜分离的的研究

参考文献：

[1] 时钧, 袁权, 高从楷. 膜技术手册[M]. 北京:化学工业出版社,2001.
[2] 徐又一, 徐志康. 高分子膜材料[M]. 北京:化学工业出版社,2005.
[3] Warkiani M E, Bhagat A S, Khoo B L, et al. Isoporous micro/nanoengineered membranes [J]. ACS Nano, 2013, 7: 1882- 1904.
[4] Tong H D, Jansen H V, Gadgil V J, et al. Silicon nitride nanosieve membrane [J]. Nano Let, 2004, 4: 283-287.
[5] Starosta W, Wawszczak D, Sartowask B, et al. Investigations of heavy ion tracks in polyethylene naphthalate films [J]. Radiat Meas, 1999, 31: 149-152.
[6] Kai Z, Xue F, Xiao S, et al. Directional photomanipulation of breath figure arrays [J]. Angew Chem Int Ed, 2014, 53: 13789-13793.
[7] Thompson G. Porous anodic alumina: Fabrication, characterization and applications [J]. Thin Solid Films, 1997, 297: 192-201.
[8] Noshay A, Mcgrath J E. Block Copolymers: Overview and Critical Survey[M]. New York: Academic Press, 1977.
[9] Jaisankar S N,Lakshminarayana Y, Ganga R. Compatibility of poly(vinyl chloride-vinyl acetate)/polyester- based polyurethane blends [J]. Polym lnt,1997,43:368-372.
[10] Moulay S. Chemical modification of poly(vinyl chloride)-Still on the run [J]. Prog Polym Sci,2010, 35, 303-331.
[11] Sneddon G, McGlynn J C, Neumann M S, et al. Aminated poly(vinyl chloride) solid state adsorbents with hydrophobic function for post-combustion CO2 capture [J]. Mater Chem A, 2014,5：11864 .
[12] Balci S, Birer O , Suzer S. Photosensitization of PVC dehydrochlorination by hydroquinone for improved optical and electrical properties [J].Polymer, 2004,45：7123-7128 .
[13] Kameda T, Ono M, Grause G, et al. Chemical modification of poly(vinyl chloride) by nucleophilic substitution [J].Polym Degrad Stab, 2009,94：107-112.
[14] Yoshinaga T,Yamaye M, Kito T, et al.Alkaline dechlorination of poly(vinyl chloride) in organic solvents under mild conditions [J]. Polym Degrad Stab,2004,86： 541-547.
[15] Park E J, Park B C, Kim Y J. Elimination and substitution compete during amination of poly(vinyl chloride) with ehtylenediamine: XPS analysis and approach of active site index[J]. Macro Res, 2018, 26(10)：913-923

服务与反馈：

【文章下载】【加入收藏】

《膜科学与技术》编辑部地址：北京市朝阳区北三环东路19号蓝星大厦邮政编码：100029 电话：010-64426130/64433466 传真：010-80485372邮箱：mkxyjs@163.com